[1]李双元,王 宏,彭渝丽,等.退火工艺对冷轧态CoCrNi中熵合金组织与性能的影响[J].西安工业大学学报,2020,(01):95-101.[doi:10.16185/j.jxatu.edu.cn.2020.01.014 ]
 LI Shuangyuan,WANG Hong,PENG Yuli,et al.Effect of Annealing on Microstructure and Properties of Cold Rolled CoCrNi Medium-Entropy Alloy[J].Journal of Xi'an Technological University,2020,(01):95-101.[doi:10.16185/j.jxatu.edu.cn.2020.01.014 ]
点击复制

退火工艺对冷轧态CoCrNi中熵合金组织与性能的影响()
分享到:

《西安工业大学学报》[ISSN:1673-9965/CN:61-1458/N]

卷:
期数:
2020年01期
页码:
95-101
栏目:
材料科学与工程
出版日期:
2020-02-15

文章信息/Info

Title:
Effect of Annealing on Microstructure and Properties of Cold Rolled CoCrNi Medium-Entropy Alloy
文章编号:
1673-9965(2020)01-095-07
作者:
李双元王 宏彭渝丽王 军武上焜
(西安工业大学 材料与化工学院,西安 710021
Author(s):
LI ShuangyuanWANG HongPENG YuliWANG JunWU Shangkun
(School of Materials and Chemical Engineering,Xi'an Technological University,Xi'an 710021,China)
关键词:
中熵合金 冷轧 退火处理 显微组织 力学性能
Keywords:
medium entropy alloys cold rolling annealing microstructure mechanical property
分类号:
TG174.4
DOI:
10.16185/j.jxatu.edu.cn.2020.01.014
文献标志码:
A
摘要:
为研究冷轧态的CoCrNi中熵合金组织与性能的演变,采用真空电弧熔炼法制备CoCrNi中熵合金并进行双辊冷轧轧制,采用不同的热处理工艺,对冷轧后的试样进行退火处理。利用扫描电子显微镜和X射线衍射仪分析其组织与结构的变化; 通过显微硬度测试和拉伸试验研究其性能变化。研究结果表明:CoCrNi中熵合金冷轧后退火处理,没有新相的产生,依然是单一FCC结构; 在退火过程中发生了再结晶现象,当退火温度为900 ℃时,由于温度较低,再结晶发生缓慢,随退火时间延长,显微硬度从456 HV降至215 HV,屈服强度从1 570 MPa降至400 MPa,塑性从5%提高至69%,组织逐渐转变为再结晶后的等轴晶; 当退火温度提高至1 000 ℃时,能快速完成再结晶,退火10 min时,显微硬度为219 HV,屈服强度和塑性分别为315 MPa和71%,随退火时间延长,组织与性能变化均无明显变化; 当退火温度继续提高至1 100 ℃时,由于退火温度较高,再结晶迅速完成,退火10 min时,显微硬度为199 HV,屈服强度和塑性分别为351 MPa和77%,随退火时间和温度的增加,发生晶粒长大,影响材料性能。
Abstract:
In order to study the effect of annealing process(above the recrystallization temperature)on the structure and properties of cold-rolled CoCrNi medium-entropy alloy,the vacuum arc melting method was used to prepare CoCrNi medium-entropy alloy for twin-roll cold rolling,and different heat treatment processes were adopted to anneal the cold-rolled samples.The changes in their microstructure were analyzed by scanning electron microscopy and X-ray diffraction,and the changes of their properties were studied through microhardness test and tensile test.The results are as follows.In the annealing treatment of the cold rolled CoCrNi medium entropy alloy,no phase transition emerged,and it remained a single FCC structure.Recrystallization occurred during annealing process.When the annealing temperature was at 900℃,the recrystallization occurred slowly due to the lower annealing temperature.With annealing time was prolonged,the microhardness decreased from 456 HV fall to 215 HV,the yield strength fell from 1 570 MPa to 400 MPa,and the plasticity increased from 5% to 69%.The structure gradually transformed into equiaxed crystals after recrystallization.When the annealing temperature rose to 1 000 ℃,the recrystallization was completed quickly.When the sample was annealed for 10 mins,its microhardness was about 219 HV,its yield strength and plasticity were 315 MPa and 71% respectively.With the annealing prolonged,there were no obvious changes in its structure and properties.When the annealing temperature continued to rise to 1 100 ℃,because of the higher temperature,the recrystallization was completed rapidly.After 10 mins annealing,the microhardness was about 199 HV,and the yield strength and the plasticity were 351 MPa and 77% respectively.With the annealing time and temperature increasing further,the grain became larger,affecting the properties of the materials.

参考文献/References:

[1] YEH J W,CHEN S K,LIN S J,et al.Nanostructured High-Entropy Alloys with Multiple Principal Elements:Novel Alloy Design Concepts and Outcomes[J].Advanced Engineering Materials,2004,6(5):299. [2] CANTOR B,CHANG I T H,KNIGHT P,et al.Microstructural Development in Equiatomic Multicomponent Alloys[J].Materials Science & Engineering:A,2004,375/376/377:213. [3] YEY F,WANG Q,LU J,et al.High-entropy Alloy:Challenges and Prospects[J].Materials Today,2016,19(6):349. [4] 梁秀兵,魏敏,程江波,等.高熵合金新材料的研究进展[J].材料工程,2009(12):75. LIANG Xiubing,WEI Min,CHENG Jiangbo,et al.Reaserch Progress in Advanced Materials of High-entropy-Alloys[J].Journal of Materials Engineering,2009(12):75.(in Chinese) [5] YOSHIDA S,BHATTACHARJEE T,BAI Y,et al.Friction Stress and Hall-Petch Relationship in CoCrNi Equi-atomic Medium Entropy Alloy Processed by Severe Plastic Deformation and Subsequent Annealing[J].Scripta Materialia,2017,134:33. [6] LIANG C H,GUO H X,ZHENG R F.The Effect of Fibrinogen on the Corrosion Behavior of CoCrNi Alloys in PBS Simulated Body Fluid[J].Rare Metal Materials and Engineering,2006,35(4):528. [7] WU Z,BEI H,OTTO F,et al.Recovery,Recrystallization,Grain Growth and Phase Stability of a Family of FCC-structured Multi-component Equiatomic Solid Solution Alloys[J].Intermetallics,2014,46:131. [8] ZHAO Y L,YANG T,TONG Y,et al.Heterogeneous Precipitation Behavior and Stacking-fault-mediated Deformation in a CoCrNi-based Medium-entropy Alloy[J].Acta Materialia,2017,138:77. [9] GLUDOVATZ B,HOHENWARTER A,THURSTON K V S,et al.Exceptional Damage-tolerance of a Medium-Entropy Alloy CrCoNi at Cryogenic Temperatures[J].Nature Communications,2016,7:10602. [10] DENG H W,XIE Z M,ZHAO B L,et al.Tailoring Mechanical Properties of a CoCrNi Medium-entropy Alloy by Controlling Nanotwin-HCP Lamellae and Annealing Twins[J].Materials Science and Engineering:A,2018,744:241. [11] WANG Z,GAO M C,MA S G,et al.Effect of Cold Rolling on the Microstructure and Mechanical Properties of Al0.25CoCrFe1.25Ni1.25 High-entropy Alloy[J].Materials Science and Engineering:A,2015,641:163. [12] SATHIYAMOORTHI P,MOON J,BAE J W,et al.Superior Cryogenic Tensile Properties of Ultrafine-grained CoCrNi Medium-entropy Alloy Produced by High-pressure Torsion and Annealing[J].Scripta Materialia,2019,163:152. [13] SATHIYAMOORTHI P,BAE J W,ASGHARI-RAD P,et al.Annealing-induced Hardening in High-pressure Torsion Processed CoCrNi Medium Entropy Alloy[J].Materials Science & Engineering:A,2018,734:338.

备注/Memo

备注/Memo:
收稿日期:2019-10-09
基金资助:国家自然科学基金(51671150); 陕西省教育厅重点实验室基金(17JS054); 陕西省自然科学基础研究计划项目(2017JM5057)。 第一
作者简介:李双元(1994-),男,西安工业大学硕士研究生。 通信作者简介:彭渝丽(1963-),女,西安工业大学教授,主要研究方向为铝镁基轻合金材料,E-mail:jupiter1963@163.com。
(编辑、校对 潘秋岑)
更新日期/Last Update: 2020-02-15